| Harris Products Group: | |||
Flux Chart |
|||
Harris 10 Flux - A powder flux for brazing and welding aluminum. Use with Harris 10 and 120 alloys. A premium formula flux, active in a range between 990ºF and 1100ºF. The powder turns to a clear liquid when the proper brazing temperature has been attained. It may also be used as a paste by adding water or alcohol. The residue is easily removed with warm water. Packaging: Six ounce plastic jar, twelve jars per carton. (010FX00) |
|||
|
Paste flux for brazing with nickel-silver and bronze alloys. Use with Harris 14, 17 and 170 alloys. Harris 17 is a premium quality water and salt flux. It is active within a temperature range of 1400ºF to 2200ºF. The flux was developed to produce exceptional capillary flow qualities for nickel-silver and bronze alloys. The residue is easily removed with warm water. If flux becomes hard, add water to bring it back to a paste consistency.
|
|||
|
Powder Flux for Zinc Die Cast. Use with Harris 52 alloy. This salt type flux is active in a temperature range from 600ºF to 1000ºF. For use on zinc die castings, pot metal and Dow metal. Packaging: Ten ounce plastic jar, twelve jars per carton. (052FX00) |
|||
|
A liquid flux for soldering with all soft solders. use Harris 505 (neutral) flux with any commercial lead-tin, tin-silver, tin-antimony soft solders. It is a general purpose, neutral, "noncorrosive" soldering flux for use on electrical devices, electronic parts, concealed joints, and for items where corrosion cannot be tolerated. It is active between 300ºF and 500ºF.
|
|||
|
A general purpose brazing flux. Use Harris 600 Flux with low fuming bronze and nickel bronze brazing alloys. This highly active powder flux has applications in brazing steel, cast irons and copper-base alloys. It is active in a heat range between 1400ºF to 2200ºF.
|
|||
AL-Braze Aluminum Brazing Flux AL-BRAZE powdered flux is recommended for use with 4047 (formerly 718) brazing alloy and other aluminum brazing alloys. It may be mixed with water or alcohol to form a paste. Meets specifications AMS3412, AWS type FB1A.
|
|||
|
A Powder Flux For Welding Cast Iron. Use Harris 800 FLUX with any commercial cast iron torch welding alloy. It is an iron oxide flux especially prepared to produce better results on "problem" cast iron. The wide active heat range of 1400ºF to 2200ºF eliminates the necessity of several different fluxes.
|
|||
|
A Powder Flux For Brazing And Welding Magnesium. use with Harris AZ61A and AZ92A magnesium alloys. Harris 900 FLUX is a special salt-powder flux formulated for magnesium. Active heat range is 950ºF to 1300ºF. It may be mixed with water or alcohol to form a paste. The residue may be removed with warm water.
|
|||
|
FOr Torch Welding Of Stainless Steel. use Harris Stainflux with all Harris stainless steel rods and other commercial chrome-nickel bearing rods. It is a superior formulation for high-temperature welding of all stainless steels.
|
|||
|
Equipment for applying flux automatically through the fuel gas flame, to
the metal, during the brazing operation. The Speed Flux Dispenser
increases production, saves gas and oxygen. It is an ideal
tool for all surface brazing applications such as automotive body shapes,
tubular steel brazing, repairing bronze castings, sculpture work, jewelry
production and many more brazing operations.
|
|||
|
For use with oxyacetylene torch only. Used with automatic fluxing devices. A boron-acetone formulation, for use in production brazing where the flux is metered through the torch and flame. It eliminates the necessity of hand applying flux on each part.
|
|||
|
The same as above but for use with all liquified petroleum gas systems such as MAPP and others.
|
|||
Stay-Clean Liquid Soldering Flux Recommended for tin/lead, tin/antimony and Stay-Brite solders; also for soldering virtually all metals (other than aluminum, magnesium or titanium). Not recommended for use in electrical or electronic applications. Stay-Clean Liquid Soldering Flux conforms to Federal Specification OF506C, Type 1, Form B. Packaging: 4 ounce flip top dispensers, 48 to the carton; 16 ounce bottles, 24 to the carton; 32 ounce bottles, 12 to the carton; 1 gallon jugs, 4 to the carton; 4 ounce brush cap dispensers, 24 to the carton.
|
|||
Stay-Clean Paste Soldering Flux An active soldering flux formulated for use with tin/lead, tin/antimony and tin/silver solders. Stay-Clean Paste Soldering Flux is a superior flux for most metals including copper, brass and bronze (not recommended for aluminum, magnesium or titanium). Stay-Clean Paste Soldering Flux should not be used for electrical or electronic applications. Stay-Clean Paste Soldering Flux conforms to Federal Specification OF506C, Type 1, Form A. Packaging: 4 ounce brush cap, 24 to the carton; 1 pound cans, 12 to the carton.
|
|||
|
Stays active to 800ºF. Bridgit flux will not burn at soldering temperatures, reducing black carbon formations that can result in voids and leaks. This flux works extremely well with Bridgit lead-free solder in potable water systems. However, this flux should work equally well with other solders. Bridgit paste flux meets all requirements of the Safe Drinking Water Act. Bridgit flux is designed primarily for copper tube applications. Packaging: 4 ounce brush cap, 24 to the carton; 1 pound containers, 12 per carton.
|
|||
STAY-SILV® Brazing Flux (White) An all purpose, low temperature flux for use in silver brazing most ferrous and nonferrous metals except aluminum, magnesium and titanium. Stay-Silv® Brazing Flux (White) is an inorganic fluoride type flux molten at 1100ºF and active to a maximum of 1600ºF. Flux residue may be removed with a hot water rinse. Meets Federal Specification OF499C, Type B; AWS Type 3A; AMS 3410F. Packaging: 4 ounce jars, 24 to the carton; 8 ounce jars, 24 to the carton; 1 pound jars, 12 to the carton; 5 pound jars, 6 to the carton; 7 ounce brush cap dispenser, 24 to the carton; 25 pound pails; 60 pound pails.
|
|||
Stay-Silv Brazing Flux (Black) Formulated for brazing applications where the work is subjected to rapid, localized heating or where longer brazing times are encountered. It is particularly useful in applications where large amounts of refractory oxides may form, such as with stainless steel alloys. The active range is 1100ºF - 1800ºF. Flux residue may be removed with a hot water rinse. Stay-Silv Brazing Flux (Black) conforms to AWS Type FB3C and AMS 3411 specifications. Packaging: 8 ounce jars, 24 to the carton; 1 pound jars, 12 to the carton; 5 pound jars, 6 to the carton; 30 pound pails, 60 pound pails.
|
|||
Dynaflow Autodispense Premium Brazing Flux A fluid-paste silver brazing flux for automated brazing of copper, brass and steel. Wide active range 1050ºF - 1600ºF and good fluidity provide excellent joint penetration. Nonflammable. Long shelf life. Good dispensing performance. Cosmetically superior.
|
|||
|
A paste flux formulated for brazing aluminum automotive and AC/R components. Easy to use, the flux residue removes easily with hot water. Nonflammable. Al-Braze E.C. Flux is also available in Powder Form.
|
|||
|
A premium auto-dispense flux for aluminum components. Flux residue is inert and noncorrosive. No post-heat cleaning required. Nonflammable. Good for conveyor-type automated brazing. Al-Braze H.Q. Flux is also available in Powder Form.
|
|||
|
Differs from Stay-Silv Brazing Flux (White) in that it is free of water, and a copper wetting agent has been added to enhance the wetting characteristics.
|
|||
|
An all-purpose, low temperature flux for use in silver brazing most ferrous and nonferrous metals (not intended for use on aluminum, magnesium and titanium). Stay-Silv #99 Powder Flux is molten at 1100ºF and active to a maximum temperature of 1600ºF. The flux residue may be removed with a hot water wash. If this is not entirely successful, a solution of dilute sulfuric acid may be employed. If the acid method is used, the assembly must be treated with a neutralizing agent such as a baking soda/water mixture.
|
|||
|
This unique backup flux for stainless steels, high chromium alloys and other alloy steels. |
|||