Diametri / imballo

Diametri		3 lb Box	4 lb Box	5 lb Box	10 lb Box	20 lb Box	50 lb Box
	015FC505POP,015FC605POP
1/4" Bare					00015910		0001590
1/4" FC					015FC90
1/8" Bare			00015600POP	00015605POP	00015610		0001560
1/8" FC		015FC603POP	015FC600POP		015FC60
1/8" FC-Blue					015FC60B
1/16" Bare			00015300POP		00015310		0001530
1/16" FC				015FC30
3/8" Bare							00015A0
3/16" Bare					00015810	00015805POP	0001580
3/16" FC					015FC80
3/32" Bare			00015500POP	00015505POP	00015510		0001550
3/32" FC		015FC503POP	015FC500POP		015FC50
5/16" Bare							0001595
5/32" Bare							0001570
5/32" FC					015FC70

Harris 15 Low-Fuming Bronze Flux-Coated Brazing Alloy

015FC500POP

Harris 15 low-fuming bronze flux-coated white brazing alloy 3/32 X 36 X 1lb package POP

DETTAGLI

Harris15 low fuming bronze is considered a “braze-welding” alloy as this copper/zinc alloy exhibits minimal capillary action during brazing. This limits joint design primarily to lap, tee, and butt joints. Butt joints require some edge preparation typically incorporating beveled edges to provide a location for filler metal to be applied and to ensure alloy penetration to the joint root. LFB was developed primarily to braze steel and some cast iron grades including malleable and grey iron. It can be used to join copper but due to its elevated melting temperature care must be taken during brazing to avoid overheating or melting the copper. It is used with the oxy-fuel process. These alloys are flux-coated. Conveniently packaged for point-of-purchase display.

Caratteristiche

Copper-zinc braze-welding flux-coated rod
Flux coating provides excellent wetting action with no objectable fuming
Exhibits minimal capillary action during brazing
Limited joint designs to lap, tee and butt joints, although butt joints require some edge preparation
Good machinability
Produces porosity-free deposits
Color matches yellow brass
Developed to braze steel and some cast iron grades, including malleable and gray iron. Also, used to join copper.
Corrosion resistance is similar to most high zinc brass alloys. Care should be taken on service conditions where water immersion is involved as dezincification is a potential issue.