Stay-Clean® Soldering Flux

SCPF4

Stay-Clean® paste soldering flux 4 oz. Jar

DETAILS

Stay-Clean® paste soldering flux was designed primarily for copper-to-copper and copper-to-brass connection. In its paste form it is ideal for soldering tube joints. It is not recommended for electrical or electronic applications due to the potential corrosive residue of the flux. This flux works well with most leaded and lead-free solder compositions. The flux residue should be removed after soldering. Conforms to the EU Reach & RoHS directive.

Features

  • Superior paste soldering flux for most metals, except aluminum, magnesium or titanium
  • Designed for copper-to-copper and copper-to-brass connections as well as copper, brass, bronze, steel, galvanized steel and Monel®.
  • Ideal for soldering tube joints
  • Works well with most leaded and lead-free solder compositions
  • Due to the corrosive nature of the flux residue, this product is not recommended for use in electrical or electronic applications
  • Complies with the EU Reach & RoHS directive

Disclaimers

Warning -

Cancer and Reproductive Harm -

www.P65Warnings.ca.gov

Warranty Information

  • 1 Year

What's Included

  • Stay-Clean® paste soldering flux 4 oz. Jar

Specifications

Consumables

Alloy Type Phos Copper
Chemical Composition Silver 5.5-6.5%
Phosphorus 5.9-6.2%
Copper Remainder %
Others (Total) 0.15%
Classification Manufactured to Harris Products Group's internal engineering standards
Density 0.305 lbs./cu.in.
Diameter 0.050 in. x 1/8 in. (1.27mm x 3.18mm)
Electrical Conductivity (%IACS) 8.80
Fluidity Rating 3
Liquidus 1470°F (799°C)
Material Phos-Copper Alloy
NSF Compliant No
Product Length 20 in.
Recommended Flux No flux is required for copper brazing. For brazing brass or copper to brass, use Stay-Silv® white flux. Harris Eco Smart™ boric acid free flux (powder or paste) is an excellent choice to promote sound brazed assemblies and comply with European REACH requirements.
Recommended Joint Clearance 0.003 in. - 0.006 in. (0.076mm - 0.152mm)
RoHS Compliant Yes
Size 28 stick tube
Solidus 1190°F (643°C)
Typical Application HVAC
Refrigeration
Joining copper or brass
Replacement for 15% alloys

Warranty

Warranty 1 Year